Technical Data Sheet

30 Litre (8 Gallon) Kits
CAT Yellow*
Tint packs coming soon.

Coverage: 7.8 m2 per litre at 150 micron WFT*
Conditions ambient/surface: 0.1°C - 45°C / 0.1°C - 70°C RH: <95%
Recommended Application Method: Plural component 1:1 ratio spray
Finish: Gloss
Pot Life: 35-40minutes
Full Cure: 1 Hour 
Critical Recoat time: 1-2 hours  
Solids: 85% (+/-1%)
Recommended Dry film thickness (per coat): 110 - 250 micron

All tests conducted on fully cured 50 micron films at room temperature:
Surface Tension, Dynes/cm: 40
Viscosity (Brookfield LVF), cps @ 25°C: 600
Specific Gravity: 1.0
Elongation: 80%
Tensile Strength: 7000 psi (48.26 mpa)
Hardness: 79 Shore D 
Taber Abrasion CS-17 wheel: 52  
Impact Resist (Direct/Reverse): 189 Nm/189 Nm
Crosshatch Adhesion (Cold Rolled Steel / Aluminium): 100%/100%
Chem resistance, 7-Day Submersion Testing:
Brake fluid: No Effect
Transmission Fluid: Slight Discolouration
Coolant: No Effect
Salt Water: No Effect
Power Steering Fluid: Slight Discolouration
Battery Acid: Damage
MEK: <200 Double Rubs
Acetone: <200 Double Rubs
Formula409: <200 Double Rubs.  

*Practical coverage will be affected by surface profile, method of application and wet film thickness applied. Higher film thickness and high overspray leads to lower coverage.


Low CorrosivePrep then;
1st Coat - PolyDTM
(min 150μm DFT)
Mild CorrosivePrep then;
1st Coat - PolyDTM  min 110μm
2nd Coat - PolyDTM min 110μm
1st Coat - Blast Saver Primer
2nd Coat - PolyDTM min 150μm
Highly CorrosivePrep then;
1st Coat - Blast Saver Primer
2nd Coat - PolyDTM min 150μm 
3rd Coat - PolyDTM min 150μm

Additional coats will increase performance. Ensure critical recoat times are honoured. Some colours may require additional coats to achieve full depth of colour.

Areas and industries of application:

Steel and concrete bridges
Boat refurbishment
Trains and carriages
Mining Equipment
Containment structures and silos
Swimming pools
Parts refurbishment
Car Park decks

polyaspartic direct to metal coating machinery coatings excavator
polyaspartic direct to metal coating machinery coatings

PolyasparticDTM-LP (PolyDTM-LP) is a long pot life version of PolyDTM, still on the leading edge of easy to use, rapid curing, direct to metal (DTM) polyaspartic coatings. It meets both current, and potential future, VOC requirements while retaining the desired fast return to service attributes that end users have come to expect from polyaspartic coatings.

Its long pot life removes the need to purchase plural component spraying equipment in order to utilise polyaspartics superior properties on your projects. 

PolyDTM-LP can be applied directly to properly prepared steel, aluminium, galvanized steel or concrete as well as to existing coatings such as epoxies and urethanes as recommended.
Even though PolyDTM-LP is designed to be DTM it’s even better over our Blast Saver Primer (BSP) which removes many prep question marks, is indefinitely re-coatable and enhances corrosion resistance. Removing any fear of corrosion taking hold before PolyDTM-LP can be applied.

Ten years ago, polyaspartic DTM coatings were considered a light to medium-duty solution for a particularly niche portion of protective coating applications. Now however, after over a decade of in-field use and advancements in formulations polyaspartics are a proven technology with demonstrated long-term performance. 

PolyasparticDTM-LP Key Features:

  • Long 40 minute potlife for use with conventional, HVLP, or airless spray systems
  • 4x higher abrasion resistance than epoxy products
  • Non-yellowing, complete UV stability
  • High gloss, glass like shine
  • Chemical, and highly corrosion resistant
  • Suitable for water immersion
  • Low viscosity
  • Solvents: 0
  • VOC (g/l): 0
  • Cures at temperatures just above Freezing
  • Dual-curing technology: Moisture + Chemical
  • Further enhanced corrosion resistance when paired with Blast Saver Primer
  • Easy mixing ratio (1:1)



Ensure all rough welds, sharp edges and weld spatter are smoothed or removed. Remove any grease, oil and other contaminants in accordance with AS1627.1. Abrasive blast clean to a minimum of AS1627.4 Class 2.5. Remove all dust and loose contaminants post blasting by brushing or compressed air, and vacuum cleaning.
Where abrasive blast cleaning is not viable: Rust, mill scale, oxide deposits and delaminating paint films must be removed by power tool cleaning according to AS1627.2. If this is also not viable use Blast Saver Primer.
Blasted surfaces should be coated within 8 hours after blasting or before rusting or other contamination of the surface occurs. If this is not possible use Blast Saver Primer, PolyasparticDTM-LP can then be applied in any amount of time required once the primer is dry.
For best results and enhanced corrosion resistance always apply Blast Saver Primer followed by PolyasparticDTM-LP 2 coats at 150 micron WFT per coat. 


Concrete should be at least 28 days old before coating. Remove all laitance, release agents, curing compounds, oil, grease, failing coatings, dust, dirt and other surface contaminants. Fill any large cracks or voids using Epoxy2U Polyurea Crack Repair or other suitable approved filler. The surface should be profiled via diamond grinding or shot blasting to ensure maximum adhesion. Moisture content of the slab should be below 5%, otherwise a moisture vapor barrier, such as Epoxy2U MVB15 should be applied prior to the PolyasparticDTM-LP coating. 

Existing Coatings

First, test adhesion of existing coating by standard cross hatch adhesion test. If the coating fails, it must be removed. If it passes, clean the surface to remove any chalking and dust. If the coating is not weathered and outside its recoat window you may need to mechanically abrade the surface to provide a key for the new coating. For best results use Blast Saver Primer on painted surfaces prior to PolyasparticDTM-LP.  

Coating performance is directly proportional to the comprehensiveness of surface preparation. 


Application can be done utilising batch mixes and airless, HVLP, conventional, or air assisted airless. Thin up to 10% with acetone or xylene (if required) to aid atomisation. 
Typical conventional spray setup:
1.8mm tip @ 50-60 psi at the gun
Typical airless setup:
Tip from 0.38 - 0.43 mm @ 80-100 psi pump pressure
1:1 plural component sprayer such as Surface Engineering Equipment PSM11, Graco XP70, or similar capable of 80 - 140 psi at the spray tip are also suitable. Use the lowest pressure possible to achieve the desired finish. Work methodically and allow adequate overlap of each pass. Do not spray an area that will take over two hours to complete before you are able to return to the starting point and begin the next coat. This ensures the first layer is within its recoat window to achieve maximum inter-coat adhesion.

Contact an appropriate equipment manufacturer for a recommendation.
This product is designed to be applied by professional trained coating applicators familiar with the application of airless, plural spray, and multi-component products.
Thinning is not required. Heating is usually not required but can be utilised at the applicators discretion.

Note: where one coat is normally required; certain colors may require additional coats to achieve full depth of colour. 


Should the coating be compromised from modifying, cutting, welding, etc. refer to the relevant substrate preparation above, then follow the additional steps below.
Ensure an area of 15-20mm at minimum around the repair is sanded with 100-200 grit sandpaper and solvent wiped down with acetone or xylene prior to re-application of PolyDTM-LP or primer.   


Read the PolyasparticDTM MATERIAL SAFETY DATA SHEET and any precautions on container labels before applying. MSDS are available from www.epoxy2u.com, www.epoxy2uaustralia.com, or by contacting info@epoxy2uaustralia.com
Keep containers closed at all times when not in use.
As with any coating; ingestion, inhalation and prolonged or repeated skin contact should be avoided by utilising good work safety practices.
Eye protection approved to AS1337 should be worn where there is a risk of splashes entering the eyes.
Always wash your hands before smoking, eating, preparing food for others, drinking or using the toilet.
Use in an area with good ventilation and avoid inhalation of atomised coatings. If risk of inhalation of coating particles exists, wear a cartridge type combined organic vapour/particulate respirator or supplied air system. When spraying, users must comply with the spray painting regulations in their country/state. In confined spaces workers must wear fresh airline respirators and comply with relevant safety regulations for working in confined spaces in your country/state.

This product is not flammable.

If welding coated surfaces, first grind off coating before welding. 
CAUTION: Read and follow all caution statements on this product data sheet and on the Material Safety Data Sheet for this product.  

Shelf Life

Shelf Life: 2 years unopened for both the Part A and B when stored inside out of direct sunlight at between 5C - 45C (40°F to 110°F). Use opened containers as soon as possible. Never leave containers open longer than is necessary.  


Any recommendation of Epoxy2U Australia contained herein, covering use, utilisation, chemical or physical properties and other qualities of the products
sold is believed reliable and considered general advice; however Epoxy2U Australia accepts no liability and makes no warranty or representation with respect thereto. Use or application is at the discretion of the Buyer without liability or obligation whatsoever of Epoxy2U Australia. Your results are your own.

Version 1 Last edited 10/12/2020